Brick Corundum/Brick Mullite Corundum
Ozi Ngwaahịa
Brick Corundums bụ ngwaahịa ndị na-anaghị emegharị ahụ nwere corundum dị ka usoro kristal mbụ, yana ọdịnaya alumina karịrị 90%.
Nhazi:A na-ekewa brik Corundum n'ime brik corundum a gwakọtara agwakọta na brik corundum a gwakọtara agwakọta. A na-eji alumina a gwakọtara agwakọta mee nke mbụ, ebe a na-eji corundum a gwakọtara agwakọta mee nke ikpeazụ. A pụkwara iji phosphoric acid ma ọ bụ ihe ndị ọzọ e ji ejikọta brik corundum eme nke na-anaghị agba ọkụ.
Àgwà Arụmọrụ:
Njirimara Refractory Dị Mma:Okpomọkụ nke brik corundum nke na-adịghị arụ ọrụ nke ọma gafere 1700°C, ụfọdụ brik chrome corundum nwekwara ike iru okpomọkụ karịrị 1790°C. Ha na-adịgide adịgide n'ebe okpomọkụ dị elu ma ghara ịdị mfe ịgbanwe ma ọ bụ mebie.
Ike Dị Elu:Ike nrụgide nke brik corundum dị ọcha nke ukwuu n'oge okpomọkụ ụlọ na-abụkarị 70MPa-100MPa, ebe nke brik chrome corundum dị elu karịrị 150MPa ma nwee ike iru 340MPa.
Ezigbo Nkwụsi Ike Kemịkalụ:Brọk corundum na-eguzogide ọgwụ acidic ma ọ bụ alkaline slag, metal, na iko gbazere agbaze nke ukwuu, ha anaghịkwa enweta mmeghachi omume kemịkalụ.
Ike siri ike megide mbuze slag:Dịka ọmụmaatụ, ihe dị na brik corundum chrome na-egbochi slag agbaze nke ọma ịbanye n'ahụ brik site na oghere capillary, na-eme ka mbuze slag dị elu megide brik corundum nkịtị.
Isi ihe ndị e ji mee ya na ihe ndị e ji emepụta ya:
Isi ihe mejupụtara brik corundum bụ alumina (Al₂O₃), nke na-agafekarị 90%, ụfọdụ nwere ruo 99%. Ihe ndị e ji arụ ọrụ gụnyere alumina sintered na corundum a gwakọtara agwakọta. Enwere ike itinye ihe ndị ọzọ dị na mineral iji mepụta ihe ndị mejupụtara ya, dịka Cr₂O₃ maka brik chrome corundum na ZrO₂ maka brik zirconium corundum.
Brọk Corundum-mullitebụ brik ndị na-anaghị emegharị ahụ nke nwere usoro abụọ dị elu nke na-adịgide adịgide: corundum (Al₂O₃) na mullite (3Al₂O₃・2SiO₂). Ha na-ejikọta ike dị elu nke corundum na ezigbo iguzogide okpomọkụ nke mullite, na-eme ka ha bụrụ ihe dị elu nke na-ahazi arụmọrụ na ịdị irè ọnụ ahịa.
Akụkụ Isi na Atụmatụ Nhazi
Ngwakọta nke usoro kristal bụ isi:Corundum na mullite bụ usoro kristal abụọ bụ isi, ọdịnaya alumina na-abụkarị site na 70% ruo 90%, ebe nke fọdụrụ bụ silicon dioxide (SiO₂). Mmetụta mmekọrịta nke usoro abụọ ahụ na-edozi arụmọrụ.
Nhazi obere ihe:A na-ekesa usoro mullite n'etiti mkpụrụ corundum n'ụdị kristal dị ka agịga ma ọ bụ kọlụm, na-emepụta usoro "skeleton corundum + njikọ mullite". Nke a abụghị naanị na ọ na-eme ka ike brik dịkwuo mma kamakwa ọ na-egbochi nrụgide okpomọkụ site na oghere micro-crystal.
Uru Arụmọrụ Dị Mkpa
Oke nguzogide okpomọkụ dị oke mma:Nke a bụ isi uru ya. Mullite nwere obere ihe na-agbasa okpomọkụ, nhazi kristal ya dị ka agịga na-amịkọrọ nrụgide nke mgbanwe okpomọkụ na-akpata, na-ebelata mgbawa nke oyi ngwa ngwa na ikpo ọkụ na-akpata n'oge okpomọkụ dị elu. Arụmọrụ ya karịrị nke brik corundum dị ọcha.
Ike ziri ezi na iguzogide nchara:Ọnụnọ nke usoro corundum na-eme ka ike dị elu ma n'ime ụlọ ma n'okpomọkụ dị elu, ebe ọ na-enyekwa ezigbo iguzogide acidic slag, iko gbazere agbaze, na ihe ndị ọzọ. Ọ bụ ezie na iguzogide alkali ya dị ntakịrị ala karịa nke brik chrome corundum, ọ na-enye ọtụtụ ojiji.
Ọkwa okpomọkụ dị ala:Ma e jiri ya tụnyere brik corundum dị elu, ọ na-enye obere ike okpomọkụ ma na-ejigide ụfọdụ ọkwa mkpuchi, na-ebelata mfu okpomọkụ na akụrụngwa dị elu ma na-eme ka ọ dabara adaba maka ngwa ndị chọrọ mkpuchi okpomọkụ.
Ndepụta Ngwaahịa
| Brịk Corundum | ||||
| NTỤKWASỊ | GYZ-99A | GYZ-99B | GYZ-98 | GYZ-95 |
| Al2O3 (%)≥ | 99 | 99 | 98 | 95 |
| SiO2 (%)≤ | 0.15 | 0.2 | 0.5 | --- |
| Fe2O3 (%)≤ | 0.10 | 0.15 | 0.2 | 0.3 |
| Porosity Apụta ìhè (%)≤ | 19 | 19 | 19 | 20 |
| Njupụta buru ibu (g/cm3)≥ | 3.20 | 3.15 | 3.15 | 3.1 |
| Ike Ịkụcha Oyi (MPa)≥ | 80 | 80 | 80 | 100 |
| Mgbanwe Ahịrị Na-adịgide Adịgide (1600° × 3h) /% | -0.2~+0.2 | -0.2~+0.2 | -0.2~+0.2 | -0.3~+0.3 |
| Mkpụgharị Ike n'okpuru Ibu (0.2MPa, 0.6%)/℃≤ | 1700 | 1700 | 1700 | 1700 |
| Brik Corundum-mullite | ||||
| NTỤKWASỊ | GMZ-88 | GMZ-85 | GMZ-80 | GYZ-75 |
| Al2O3 (%)≥ | 88 | 85 | 80 | 75 |
| Fe2O3 (%)≤ | 0.8 | 1.0 | 1.0 | 1.2 |
| Porosity Apụta ìhè (%)≤ | 15(17) | 16(18) | 18(20) | 18(20) |
| Njupụta buru ibu (g/cm3)≥ | 3.00 | 2.85 | 2.75 | 2.60 |
| Ike Nkụcha Oyi (MPa) | 100-120 | 80-100 | 80-100 | 60-80 |
| Mgbanwe Ahịrị Na-adịgide Adịgide (1600° × 3h) /% | -0.1~+0.1 | -0.1~+0.1 | -0.2~+0.2 | -0.2~+0.2 |
| Mkpụgharị Ike n'okpuru Ibu (0.2MPa, 0.6%)/℃≤ | 1700 | 1680 | 1650 | 1650 |
Ngwa
Ojiji nke brik Corundum:
Ụlọ ọrụ ígwè:A na-eji ya maka ihe eji agbaze ihe dị oke ọkụ dịka ihe ntụgharị, ihe ọkụ eletrik, na ihe eji eme ka ihe dị nro, yana ihe ndị dị ka ihe ndọda, ihe mgbochi, na sistemụ ịgbapụta ihe maka ịtụba ihe na-aga n'ihu.
Ịgbaze ígwè na-abụghị ferrous:A na-etinye ya n'ime ọkụ ọkụ na-agbaze ma na-eme ka ọ dị ọcha maka ọla ndị na-abụghị ígwè dịka aluminom, ọla kọpa, na nickel.
Ụlọ ọrụ iko:A na-ejikarị ya eme ihe na brik checker n'ime ụlọ regenerator na ọdụ ụgbọ mmiri chaja nke ọkụ ọkụ iko na-agbaze.
Ụlọ ọrụ simenti:A na-agba ya n'ime ebe a na-agba ọkụ nke simenti rotary kilns.
Ụlọ ọrụ kemịkalụ:Ejiri igwe na-eme ka okpomọkụ dị elu na ọkụ ọkụ gbawaa agbawa kpuchie ya.
Ụlọ Ọrụ Ike:Ejiri ngwa ọgwụgwọ gas na ihe ndị na-eme ka gas dị ọkụ dị elu kpuchie ya.
Ojiji Ndị Dị Mkpa nke Brick Mullite Corundum
Ụlọ ọrụ simenti:A na-ekpuchi ya n'ime mpaghara mgbanwe na precalciner nke simenti rotary kilns. Ha nwere ike iguzogide nnukwu mgbanwe okpomọkụ n'ime rotary kiln ebe ha na-eguzogide gas ndị na-emebi emebi nke ire ere nke ihe ndị e ji simenti mee.
Ụlọ ọrụ iko:A na-eji brik ndị na-enyocha ihe na-eme ka ọkụ glass sie ike na mgbidi dị n'akụkụ ọkụ, ha na-eguzogide mgbanwe okpomọkụ ugboro ugboro, iko agbaze anaghịkwa emebi ngwa ngwa.
Ụlọ ọrụ Metallurgy na Chemical:Ọ dị mma maka ojiji n'ebe okpomọkụ dị n'etiti na nke dị ala nke ebe a na-ere ọkụ na-anaghị agbaze ígwè, ihe mkpuchi ọkụ na-agbaze ọkụ nke dị elu, na ngwa e ji eme ka ihe na-akpali akpali na ụlọ ọrụ kemịkalụ, na-edozi ike na ihe achọrọ maka iguzogide ujo okpomọkụ.
Nkọwapụta Ụlọ ọrụ
Shandong Robert New Material Co., Ltd.dị na Zibo City, Shandong Province, China, nke bụ ebe mmepụta ihe na-adịghị agbanwe agbanwe. Anyị bụ ụlọ ọrụ ọgbara ọhụrụ nke na-ejikọta nyocha na mmepe, mmepụta, ire ere, imewe na owuwu nke ọkụ, teknụzụ, na ihe ndị na-adịghị agbanwe agbanwe mbupụ. Anyị nwere akụrụngwa zuru oke, teknụzụ dị elu, ike teknụzụ siri ike, ịdị mma ngwaahịa dị mma, na aha ọma. Ụlọ ọrụ mmepụta anyị na-ekpuchi ihe karịrị eka 200 na mmepụta kwa afọ nke ihe ndị na-adịghị agbanwe agbanwe dị ihe dị ka tọn 30000 na ihe ndị na-adịghị agbanwe agbanwe na-adịghị agbanwe agbanwe bụ tọn 12000.
Isi ngwaahịa anyị nke ihe ndị na-adịghị agbanwe agbanwe gụnyere: ihe ndị na-adịghị agbanwe agbanwe nke alkaline; ihe ndị na-adịghị agbanwe agbanwe nke silicon aluminom; ihe ndị na-adịghị agbanwe agbanwe nke na-adịghị agbanwe agbanwe; ihe ndị na-adịghị agbanwe agbanwe nke na-eme ka ihe ghara ịdị ọcha; ihe ndị na-adịghị agbanwe agbanwe pụrụ iche; ihe ndị na-adịghị agbanwe agbanwe nke na-arụ ọrụ maka sistemụ ihe ndị na-aga n'ihu.
Ajụjụ Ndị A Na-ajụkarị
Ị chọrọ enyemaka? Jide n'aka na ị gara na ebe nkwado anyị maka azịza nye ajụjụ gị!
Anyị bụ ezigbo ndị nrụpụta ihe, ụlọ ọrụ mmepụta ihe anyị bụ ọkachamara n'ịmepụta ihe ndị na-anaghị emegharị ahụ ruo ihe karịrị afọ iri atọ. Anyị na-ekwe nkwa inye ọnụahịa kacha mma, ọrụ kacha mma tupu ere na mgbe erechara ya.
Maka usoro mmepụta ọ bụla, RBT nwere usoro QC zuru oke maka ihe mejupụtara kemịkalụ na ihe ndị dị na ya. Anyị ga-anwale ngwaahịa ndị ahụ, a ga-ebugakwa asambodo ịdị mma ya na ngwaahịa ndị ahụ. Ọ bụrụ na ị nwere ihe pụrụ iche achọrọ, anyị ga-agbalịsi ike ime ka ha kwekọọ.
Dabere na ọnụọgụgụ, oge nnyefe anyị dị iche. Mana anyị na-ekwe nkwa izipu ya ozugbo enwere ike yana ịdị mma a na-ekwe nkwa.
N'ezie, anyị na-enye ihe nlele n'efu.
Ee, n'ezie, a na-anabata gị ịga leta ụlọ ọrụ RBT na ngwaahịa anyị.
Enweghị oke, anyị nwere ike inye ndụmọdụ na ngwọta kacha mma dịka ọnọdụ gị si dị.
Anyị anọwo na-emepụta ihe ndị na-anaghị emegharị ahụ ihe karịrị afọ iri atọ, anyị nwere nkwado teknụzụ siri ike na ahụmịhe bara ụba, anyị nwere ike inyere ndị ahịa aka ịmepụta ebe dị iche iche ma nye ọrụ otu nkwụsị.