Ụlọ ọrụ AZS
| NgwaahịaAha | Ụlọ ọrụ AZS |
| Nkọwa | A na-akpọkwa ngọngọ AZS fused zirconia corundum brik nke nwere Al2O3-ZrO2-SiO2.Ihe nkedo AZS a jikọtara ọnụ bụ nke alumina ntụ ntụ dị ọcha na ájá zircon (nke nwere 65% zirconia na 34% SiO2).Mgbe agbazechara alumina ntụ ntụ na ájá zircon n'ime ọkụ eletrik, a na-atụba ha n'ụdị dị iche iche wee mee ka ọ dị jụụ ka ọ bụrụ ihe siri ike. |
| Nlereanya | AZS-33/AZS-36/AZS-41 |
| Nha | Standard size: 230 x 114 x 65mm, pụrụ iche size na OEM ọrụ na-enyekwa! |
| Atụmatụ | 1. High refractoriness; 2. Ezi nguzogide ujo thermal; 3. Ezi ihe na-eguzogide ihe; 4. Ezi nkwụsi ike nke kemịkal; 5. Ezi ike okpomọkụ dị elu na nkwụsi ike olu. 6. Nnukwu mgbochi mbuze |
Foto nkọwa
Brick kwụ ọtọ
Bricks Checker
Bricks akpụrụ akpụ
Bricks akpụrụ akpụ
Bricks akpụrụ akpụ
Bricks akpụrụ akpụ
Usoro nkedo
| Nlereanya | AZS-33 | ||
| Usoro nkedo | Nkọwa | Njupụta (g/cm3) | Ngwa |
| Nkedo nkịtị (PT) | Ọ bụ usoro nkedo a na-ahụkarị, na oghere mbelata nke ngwaahịa ahụ dị n'akụkụ ala nke ọdụ ụgbọ mmiri nkedo. | ≥3.40 | Obere stovu elu;ọdọ mmiri na-agbaze;nri ọdụ ụgbọ mmiri;mpaghara kọntaktị na-abụghị iko |
| Nkedo tilt(QX) | A na-anabata usoro nkedo nke nwere mmasị, na oghere shrinkage nke ngwaahịa ahụ na-adabere na njedebe dị ala, nke a na-ejikarị dị ka brik mgbidi ọdọ mmiri. | ≥3.40 | mgbidi ọdọ mmiri na-agbaze |
| Ọ nweghị ihe nkedo ọgbaghara (WS) | Ngwaahịa na-enweghị mbelata nke nwere oghere mbelata ewepụrụ na brik nkedo | ≥3.70 | Mgbidi dị n'akụkụ, ọnụ ụlọ kiln, pavement, brik nwere ụdị pụrụ iche |
| Nkedo n'efu nke Quasi Shrinkage(ZWS) | Yiri nkedo na-abụghị nke mbelata, a na-ewepụ oghere mbelata nke brik nkedo. | ≥3.60 | mgbidi ọdọ mmiri na-agbaze |
| Nlereanya | AZS-36 | ||
| Usoro nkedo | Nkọwa | Njupụta (g/cm3) | Ngwa |
| Nkedo nkịtị (PT) | Ọ bụ usoro nkedo a na-ahụkarị, na oghere mbelata nke ngwaahịa ahụ dị n'akụkụ ala nke ọdụ ụgbọ mmiri nkedo. | ≥3.50 | Obere stovu elu;ọdọ mmiri na-agbaze;nri ọdụ ụgbọ mmiri;mpaghara kọntaktị na-abụghị iko |
| Nkedo tilt(QX) | A na-anabata usoro nkedo nke nwere mmasị, na oghere shrinkage nke ngwaahịa ahụ na-adabere na njedebe dị ala, nke a na-ejikarị dị ka brik mgbidi ọdọ mmiri. | ≥3.50 | mgbidi ọdọ mmiri na-agbaze |
| Ọ nweghị ihe nkedo ọgbaghara (WS) | A na-ewepụ akụkụ oghere shrinkage nke brik nkedo kpamkpam. | ≥3.80 | Mgbidi ọdọ mmiri na-agbaze, efere ala, brik pụrụ iche |
| Nkedo n'efu nke Quasi Shrinkage(ZWS) | Yiri nkedo na-abụghị nke mbelata, a na-ewepụ oghere mbelata nke brik nkedo. | ≥3.70 | mgbidi ọdọ mmiri na-agbaze |
| Nlereanya | AZS-41 | ||
| Usoro nkedo | Nkọwa | Njupụta (g/cm3) | Ngwa |
| Enweghị Mbelata oghereNkedo(WS) | Yiri nke na-enweghị isi, oghere mbelata nke brik nkedo bụ kpamkpamwepụrụ. | ≥3.90 | mgbidi ọdọ mmiri na-agbaze;oghere mmiri na-asọ asọ;akuku ọdụ ụgbọ mmiri;brik na-afụ ụfụ;ikpo ọkụ;brik oghere electrode;brik pụrụ iche |
| KwụsịMbelata N'efuNkedo (ZWS) | N'ụzọ bụ isi bepụ oghere shrinkage nke brik nkedo | ≥3.85 | mgbidi ọdọ mmiri na-agbaze |
Ndekọ ngwaahịa
| Ihe | AZS33 | AZS36 | AZS41 | |
| Ngwakọta kemịkalụ(%) | Al2O3 | ≥50.00 | ≥49.00 | ≥45.00 |
| ZrO2 | ≥32.50 | ≥35.50 | ≥40.50 | |
| SiO2 | ≤15.00 | ≤13.50 | ≤12.50 | |
| Na2O+K2O | ≤1.30 | ≤1.35 | ≤1.30 | |
| Njupụta buru ibu (g/cm3) | ≥3.75 | ≥3.85 | ≥4 | |
| Prọsity pụtara (%) | ≤1.2 | ≤1.0 | ≤1.2 | |
| Ike Nchicha oyi (Mpa) | ≥200 | ≥200 | ≥200 | |
| Oke nkewa afụ (1300ºC*10h) | ≤1.2 | ≤1.0 | ≤1.0 | |
| Okpomọkụ nke oge iko (ºC) | ≥1400 | ≥1400 | ≥1410 | |
| Ọnụego mgbochi corrosion nke iko mmiri mmiri 1500ºC*36h(mm/24h)% | ≤1.4 | ≤1.3 | ≤1.2 | |
| Njupụta pụtara ìhè (g/cm3) | PT (RN RC N) | ≥3.55 | ≥3.55 | ≥3.70 |
| ZWS(RR EVF EC ENC) | ≥3.65 | ≥3.75 | ≥3.85 | |
| WS (RT VF EPIC FVP DCL) | ≥3.75 | ≥3.80 | ≥3.95 | |
| QX(RO) | ≥3.65 | ≥3.75 | ≥3.90 | |
Ngwa
| Nlereanya | ZrO2 | Ngwa |
| AZS 33 | 33% | Nnukwu microstructure nke AZS33 na-eme ka brik ahụ nwee ezigbo nguzogide mmiri mmiri mmiri, ọ dịghịkwa mfe ịmepụta nkume ma ọ bụ ntụpọ ndị ọzọ na iko iko.Ọ bụ ngwaahịa a na-ejikarị n'ọkụ na-agbaze iko, ọ dịkwa mma maka usoro elu nke ọdọ mmiri na-agbaze, brik mgbidi ọdọ mmiri na brik nke ọdọ mmiri na-arụ ọrụ, na ihu ihu, wdg. |
| AZS36 | 36% | Na mgbakwunye na inwe otu eutectic dị ka AZS33, brik AZS36 nwere ihe agbụ-dị ka kristal zirconia na ọdịnaya nke iko dị ala, yabụ na-abawanye nguzogide corrosion nke brik AZS36, ya mere ọ dabara maka mmiri mmiri iko na ọnụego ọsọ ọsọ.ma ọ bụ ebe okpomọkụ dị elu. |
| AZS41 | 41% | Na mgbakwunye na eutectics nke silica na alumina, ọ nwekwara ọtụtụ kristal zirconia ekesara n'otu n'otu.Na usoro brik corundum zirconium, ọ nwere ezigbo nguzogide corrosion.Ya mere, a na-ahọrọ akụkụ ndị bụ isi nke ọkụ iko ahụ iji dozie ndụ nke akụkụ ndị a na akụkụ ndị ọzọ. |
Glass sere n'elu
Igwe ọgwụ
Igwe eji eme ihe kwa ụbọchị
Glass ọkwa nri
Ngwugwu & Ụlọ nkwakọba ihe
Ajụjụ a na-ajụkarị
Achọrọ enyemaka?Jide n'aka na ịga na forums nkwado anyị maka azịza nye ajụjụ gị!
Anyị bụ ezigbo emeputa, ụlọ ọrụ anyị bụ ọkachamara na-emepụta ihe refractory maka ihe karịrị afọ 30.Anyị na-ekwe nkwa ịnye ọnụahịa kacha mma, ọrụ izizi ahịa na mgbe irechara.
Maka usoro mmepụta nke ọ bụla, RBT nwere usoro QC zuru ezu maka ihe mejupụtara kemịkalụ na ihe anụ ahụ.Na anyị ga-anwale ngwongwo ndị ahụ, a ga-ebufekwa akwụkwọ ikike na ngwaahịa.Ọ bụrụ na ị nwere ihe pụrụ iche chọrọ, anyị ga-agbalị ike anyị niile ịnabata ha.
Dabere na ọnụ ọgụgụ, oge nnyefe anyị dị iche.Ma anyị na-ekwe nkwa ibupu ngwa ngwa o kwere omume na mma ekwe nkwa.
N'ezie, anyị na-enye free samples.
Ee, n'ezie, ị na-anabata ileta RBT ụlọ ọrụ na anyị ngwaahịa.
Enweghị oke, anyị nwere ike ịnye ndụmọdụ na ngwọta kachasị mma dịka ọnọdụ gị si dị.
Anyị na-eme ihe refractory ihe karịrị afọ 30, anyị nwere nkwado teknụzụ siri ike na ahụmahụ bara ụba, anyị nwere ike inyere ndị ahịa aka ịmepụta kilns dị iche iche ma nye otu nkwụsị ọrụ.